Determination of Scattering and Absorption Coefficients for Plasma‐Sprayed Yttria‐Stabilized Zirconia Thermal Barrier Coatings

Prediction of radiative transport through translucent thermal barrier coatings (TBCs) can only be performed if the scattering and absorption coefficients and index of refraction of the TBC are known. To date, very limited information on these coefficients, which depend on both the coating composition and the microstructure, has been available for the very commonly utilized plasma‐sprayed 8 wt% yttria‐stabilized zirconia (8YSZ) TBCs. In this work, the scattering and absorption coefficients of freestanding plasma‐sprayed 8YSZ coatings were determined from room‐temperature normal‐incidence directional‐hemispherical reflectance and transmittance spectra over the wavelength range from 0.8 to 7.5 μm. Spectra were collected over a wide range of coating thickness from 60 to almost 900 μm. From the reflectance and transmittance spectra, the scattering and absorption coefficients as a function of wavelength were obtained by fitting the reflectance and transmittance values predicted by a four flux model to the experimentally measured values at all measured 8YSZ thicknesses. While the combined effects of absorption and scattering were shown in general to exhibit a nonexponential dependence of transmittance on specimen thickness, it was shown that for sufficiently high absorption and optical thickness, an exponential dependence becomes a good approximation. In addition, the implications of the wavelength dependence of the plasma‐sprayed 8YSZ scattering and absorption coefficients on (1) obtaining accurate surface‐temperature pyrometer measurements and on (2) applying mid‐infrared reflectance to monitor TBC delamination are discussed.